Ferrite Mix Selection - Palomar Engineers®

Ferrite Mix Selection Guide – RFI / EMI Suppresion from KHz to GHZ

Palomar Engineers® helps you select the proper ferrite mix for your RFI/EMI suppression, transformer, or choke application — from 150 kHz to 1 GHz — using proven mixes 31, 43, 52, 61, 73, 75, and 77.

Material Types

Ferrite materials are generally divided into two primary groups, each designed for different frequency ranges and performance characteristics:

Nickel-Zinc (NiZn) Ferrites — Mix 43, 52, 61
These materials have a low permeability range (20 – 850 µ) and are characterized by high resistivity, moderate temperature stability, and high Q-factors.
- Ideal frequency range: 500 kHz – 100 MHz
- Excellent for low-power, high-inductance resonant circuits, and wideband transformers.
- NiZn ferrites perform best from 2 MHz up to several hundred MHz, making them the preferred choice for most baluns, ununs, and high-frequency RFI/EMI suppression.
- Note: For common-mode inductors, NiZn materials are effective from approximately 70 MHz to several GHz.
Manganese-Zinc (MnZn) Ferrites — Mix 31, 73, 75
With higher permeability values (typically above 850 µ), MnZn ferrites exhibit lower resistivity, moderate saturation flux density, and excellent low-frequency performance.
- Ideal frequency range: 1 kHz – 1 MHz
- Commonly used in switch-mode power transformers (20 – 100 kHz) and low-frequency RFI/EMI suppression.
- Effective for reducing unwanted RF noise from 2 MHz – 250 MHz.
- Recommended for inductor applications below 5 MHz, especially for common-mode chokes where MnZn impedance performs best up to 10 MHz.

Summary Tip:

Use NiZn (Mix 43, 52, 61) for broadband, high-frequency applications.
Use MnZn (Mix 31, 73, 75) for low-frequency, high-impedance RFI suppression and power filtering.

<Material Types

There are two basic ferrite material groups: (1) Those having a permeability range from 20 to 850 µ are of the Nickel Zinc (NiZn) class (mix 43, 52, 61), and (2) those having initial permeabilities above 850 µ are usually of the Manganese Zinc (MnZn) class (Mix 31, 73, 75).

The NiZn ferrite cores (mix 43, 52, 61) have low permeability, exhibit high volume resistivity, moderate temperature stability and high ‘Q’ factors for the 500 KHz to 100 MHz frequency range. They are well suited for low power, high inductance resonant circuits. Their low permeability factors also make them useful for wide band transformer applications. Nickel-zinc ferrites have a higher resistivity and are used at frequencies from 2 MHz to several hundred megahertz. The exception is common mode inductors where the impedance of NiZn material is recommended from 70 MHz to several hundred GHz.

The MnZn ferrite cores (Mix 31, 73, 75) have high permeabilities above 800 µ, have fairly low volume resistivity and moderate saturation flux density. They offer high ‘Q’ factors for the 1 KHz to 1 MHz frequency range. Cores from this group of materials are widely used for switched mode power conversion transformers operating in the 20 KHz to 100 KHz frequency range. These cores are also very useful for the attenuation of unwanted RF noise signals in the frequency range of 2 MHz to 250 MHz. Manganese-zinc ferrites are generally used in inductor applications where the operating frequency is less than 5 MHz. The exception is common mode inductors where the impedance of MnZn material makes it the best choice up to 10 MHz>

Two Primary Ferrite Families

Manganese-Zinc (MnZn) — Mix 31, 73, 75, 77
- High permeability (>850 µ)
- Best for low-frequency RFI/EMI suppression (150 kHz – 10 MHz)
- Commonly used for common-mode chokes, feed line chokes, and low-band HF applications
- Provides high impedance at lower frequencies and is ideal for power line and HF noise suppression
Nickel-Zinc (NiZn) — Mix 43, 52, 61
- Lower permeability (20 – 850 µ)
- Performs best at higher frequencies (2 MHz – 1 GHz)
- Preferred for baluns, ununs, and broadband transformers where wide frequency response is important
- Excellent for VHF and UHF RFI filtering and high-frequency isolation transformers

Palomar Engineers® Mix Selection

Palomar Engineers® uses the industry’s most proven ferrite compositions — Mix 31, 43, 52, 61, 73, 75, and 77 — to cover virtually all RFI/EMI, choke, and transformer applications.

Each mix has a defined permeability and recommended frequency range to match specific uses such as:

RFI/EMI common-mode suppression
Multi-ratio toroid baluns and ununs
Feed line isolation chokes
Broadband impedance transformers

The following table (below) summarizes our recommended ferrite mixes and their effective frequency ranges for best performance.

<What’s Different between Mixes?

The “Mix” is the chemical formula of the iron oxide. Ferrite is a ceramic consisting of iron oxide and generally either of two types:

Manganese-zinc (MnZn) available as Mix #31, #75 and #77 (and others) – work well for common mode chokes
Nickel-Zinc (NiZn) available as Mix #43, #52, #61, (and others) – generally preferred material for baluns/ununs

Palomar Engineers uses mix 31, 43, 52, 61, 73, 75 and 77 for most applications from RFI/EMI common mode suppression, multi-ratio toroid baluns and ununs and sleeve baluns for line isolation. Each mix number has a measurable permeability and suggested frequency range for certain applications.

The table below gives our recommended applications for various mixes and effective frequency ranges>

Mix #	Material	Initial Permeability	RFI/EMI Common Mode Suppression Range	Tuned Circuits – Coil	Wide Band Transformer
31 (1)	MnZn	1500	1-300 MHz	–	1:1 only, <300 MHz
43 (2)	NiZn	800	25-300 MHz	< 10 MHz	3-60 MHz
52 (6)	NiZn	250	200-1000 MHz	< 20 MHz	1-60 MHz
61 (3)	NiZn	125	200-1000 MHz	<100 MHz	1-300 MHz
73 (7)	MnzN	2500	< 50 MHz	< 2 MHz	<10 MHz
75/J (4)	MnZn	5000	150 KHz – 10 MHz	< .75 MHz	.1-10 MHz

Notes

(1) Mix 31 excellent for 1-10 MHz common mode suppression, then about same as 43 up to 250 MHz, NOT recommended for multi-ratio impedance transformers (baluns/ununs) due to material characteristics and power handling capability – ok for ham radio 1:1 feed line choke applications. Curie temperature >130 C. Mix 31 is available in TOROIDS, SLIP ON BEADS, and SNAP ON SPLIT BEADS

(2) Mix 43 excellent for common mode chokes from 25-300 MHz, Use Mix 31 below 10 MHz for higher choking impedance. Curie temperature >130 C.. Mix 43 is available in TOROIDS, and SLIP ON BEADS

(3) Mix 61 will withstand high power in multi ratio (2:1, 4:1, 9:1) impedance transformers (baluns/ununs). Currie temperature > 300 C. Mix 61 is available in TOROIDS, SLIP ON BEADS, and SNAP ON SPLIT BEADS

(4) Mix 75 (also known as Mix J) is a high permeability MnZn ferrite intended for a range of broadband and pulse transformer applications and common-mode inductor designs. Excellent for common mode suppression on AM broadcast frequencies from 500 KHz-1.8 MHz. Also very useful for medical instrument transducer isolation, inverter assemblies, inductive motors and control units. Curie temperature >140 C. Mix 75 is available in TOROIDS, SLIP ON BEADS, ,and SNAP ON SPLIT BEADS,

Optimized to solve low-frequency EMI issues between 150 kHz and 10 MHz
Suppresses common-mode noise up to 30 MHz
Replaces expensive line filters to mitigate conducted noise
Split core performance closely resemble solid cores, allowing seamless transitions from test to production

Applications:

Automotive: Inverter assemblies, inductive motors
Consumer Electronics: Power supplies, peripheral cables
Medical: Transducer isolation, human-machine interfaces
White Goods: Control units, motors

(6) The Jerry Sevick, W2FMI broadband transformers (baluns/ununs) used a permeability of 250 (Mix 52) and the F240-52 ring toroids are ideal for replicating his designs.

(7) Mix 73 only available in small bead size, for larger inside diameter requirements, use mix 75 or 77

General comment on frequency ranges and application use

When selecting a mix to use for tuned circuits or broadband transformers, the frequency range should allow for operation in the INDUCTIVE range of the ferrite mix frequency curve. For best results use the proper mix with RESISTIVE dominate range for RFI/EMI suppression at the fundamental RFI frequency. Mix 31 is only appropriate for 1:1 impedance transformers and for RFI suppression from 1-300 MHz and should not be used for <1:1 or > 1:1 impedance transformers as the material resistivity is high over 5 MHz. We have experienced excellent RFI common mode suppression under 5 MHz with mix 75 and mix 77 using multi-turn toroidal topology.

ferrite beads fig01 1024x429 - Ferrite Mix Selection

Palomar Engineers FB102-31 Impedance Curves (below)

FB102 31 Z Rs XL - Ferrite Mix Selection

RFI/EMI Suppression Range Mix Comparison

(Palomar Engineers FB56-31, FB-56-43, FB56-46, FB56-61, FB56-75)

Toroid Mix Comparison Graph 1 - Ferrite Mix Selection

Download Fair-Rite Material Specifications Sheet for 31, 43, 52, 61, 75 – CLICK HERE

For RFI/EMI suppression remember to select the mix which includes the INTERFERING signal frequency. E.g. if AM broadcast is affecting your 7 MHz ham receiver, choose mix 75 which is effective at AM broadcast frequency RFI choking. If your 160 meter signal is affecting your DSL or computer try mix 75 (F240-75) on the power line to the effected device as well as the signal source as the AC line often acts as an “antenna” at these frequencies picking up common mode current.

Download Fair-Rite MSDS Safety Sheet for 31, 43, 52, 61, 75 – CLICK HERE

RFI/EMI Suppression Comparison of Mix 75 and Mix 31 for under 5 MHz:

What is Ferrite?

Ferrite is a class of ceramic material with useful electromagnetic properties and an interesting history (see below). Ferrite is rigid and brittle. Like other ceramics, ferrite can chip and break if handled roughly. Luckily it is not as fragile as porcelain and often such chips and cracks will be merely cosmetic. Ferrite varies from silver gray to black in color. The electromagnetic properties of ferrite materials can be affected by operating conditions such as temperature, pressure, field strength, frequency and time.

There are basically two varieties of ferrite: soft and hard. This is not a tactile quality but rather a magnetic characteristic. ‘Soft ferrite’ does not retain significant magnetization whereas ‘hard ferrite’ magnetization is considered permanent. Fair-Rite ferrite materials are of the ‘soft’ variety.

Ferrite has a cubic crystalline structure with the chemical formula MO^.Fe₂O₃where Fe₂O₃is iron oxide and MO refers to a combination of two or more divalent metal (i.e: zinc, nickel, manganese and copper) oxides. The addition of such metal oxides in various amounts allows the creation of many different materials whose properties can be tailored for a variety of uses.

Ferrite components are pressed from a powdered precursor and then sintered (fired) in a kiln. The mechanical and electromagnetic properties of the ferrite are heavily affected by the sintering process which is time-temperature-atmosphere dependent.

Ferrite shrinks when sintered. Depending on the specific ferrite, this shrinkage can range from 10% to 17% in each dimension. Thus the unfired component’s volume may be as much as 60% larger than the sintered value. Maintaining correct dimensional tolerances as well as the prevention of cracking and warpage related to this shrinkage are fundamental concerns of the manufacturing process.

A Short History of Ferrites

The history of ferrites (magnetic oxides) began centuries before the birth of Christ with the discovery of stones that would attract iron. The most plentiful deposits of these stones were found in the district of Magnesia in Asia Minor, hence the mineral’s name became magnetite (Fe₃O₄).

Much later, the first application of magnetite was as ‘Lodestones‘ used by early navigators to locate magnetic North. In 1600 William Gilbert published De Magnete, the first scientific study of magnetism. In 1819 Hans Christian Oersted observed that an electric current in a wire affected a magnetic compass needle. With further contributions by Faraday, Maxwell, Hertz and many others, the new science of electromagnetism developed.

Naturally occurring magnetite is a weak ‘hard’ ferrite. ‘Hard’ ferrites possess a magnetism which is essentially permanent. In time, man-made ‘hard’ ferrites with superior properties were developed but producing an analogous ‘soft’ magnetic material in the laboratory proved elusive.

During the 1930’s research on ‘soft’ ferrites continued, primarily in Japan and the Netherlands. However, it was not until 1945 that J. L. Snoek of the Phillips Research Laboratories in the Netherlands succeeded in producing a ‘soft’ ferrite for commercial applications. Originally manufactured in a few select shapes and sizes, primarily for inductor and antenna applications, ‘soft’ ferrite has proliferated into countless sizes and shapes for a multitude of uses. Ferrites are used predominately in three areas of electronics: low level applications, power applications, and Electro-Magnetic Interference (EMI) suppression.

Frequently Asked Questions (FAQ)

Q: Do I need to protect the parts in an outdoor application?

A: Ferrite material by itself (no conductor or plastic enclosure) is fairly inert when it comes to adverse environmental conditions, electrical properties do change with temperature. Concern with conductors is the same as with any other electronic component. Plastic cases are polypropylene and can degrade with UV exposure over time, additionally the plastic cased parts are not really intended for outdoor or extreme temperature installations. If used in such environments: it would be judicious to wrap a robust tape, nylon cable tie or other holding mechanism around the plastic case for security as the plastic can deform at temperatures below 0 deg C. or above +85 deg C.

Q: How are solid cores secured to a cable?

A: Typical solutions are a tie wrap on the cable at each end of the core, over mold, heat shrink tubing or tape.

Q: Can you supply the ECCN (Export Control Classification Number)?

A: EAR99

Q: What is the max temperature that a ferrite core can be subjected to before permanent damage occurs?

A: Generally speaking it is the material type’s Curie Temperature, where the ferrite loses its magnetic properties; when the temperature returns to below Curie, the magnetic properties return but, in some instances, not to where they were before the exposure to high temperature. Physically, electrical and magnetic performance aside, ferrites can withstand temperatures in excess of 1000 deg C without melting but can crack due to fast temperature change.

Q: Do I need to protect the parts in an outdoor application?

Above History and Q & A from Fair-rite.com